METHODS EMPLOYED.
It may be well to state briefly the methods I employed in detecting the real character of the material. The fibers were first viewed under plain transmitted light, secondly, polarized light and selenite plate. Since silk and cotton are polarizing bodies, "cottonized silk," if such could be made as described, would give, in this case, the prismatic colors of both fibers, and the complementary colors would differ greatly because of the great disparity of their respective polarizing and refractive powers.
The fact will be observed that a cotton fiber presents the appearance of a twisted ribbon when viewed by the microscope, while silk, owing to its cylindrical form, cannot twist on itself. It should also be considered that the diameter of "cottonized silk," so called, would be greater than that of a fiber of silk, because the silk solution would have to be applied to an actual thread of cotton, and not to a single cotton fiber, by reason of the shortness of the original hairs of the latter. Were a single fiber of such a combination put under a suitable objective, and a drop of nitric acid brought in contact with the fiber, it would be seen that the acid would destroy the silk and leave the fibers of cotton untouched, the latter being insoluble in cold nitric acid. The action of muriatic acid is similar in this respect. Were a fiber of cotton present and a drop of pure sulphuric acid placed on it, followed quickly by a drop of a transparent solution of the tincture of iodine, a peculiar change in the fiber would take place, provided the right proportion of acid be used. Cotton fiber, and especially flax fiber, under such conditions, forms into disks or beads of a beautiful blue color.
Fig. 1 represents a cotton fiber, and 2, 3, 4, 5 those of flax, as they appear under the acid treatment. Every textile amylaceous fiber is convertible into these forms, more or less, by strong sulphuric acid. The fibers of cotton, flax, and ramie are examples of amylaceous cellulose, that is to say, these fibers are converted into starchy matter by treatment with the last-named acid. Therefore combinations of these fibers in any composition of non-amylaceous fiber (ligneous or woody fiber) will be dissolved, leaving the latter unharmed; the woody fibers remaining will prove suitable objects for examination under the microscope.