[9] Cornices and other architectural ornaments, remarkable for their lightness and beauty, are stamped out of sheet zinc. Zinc-roofing does not require painting, but it melts during a conflagration, and even burns at a strong heat. Many iron vessels, &c., are covered with zinc (‘galvanised’) in order to prevent them from rusting.
[10] Veeren (1891) proved this by simple experiments, finding that in vacuo the solution proceeds far more rapidly for both pure and commercial zinc, and still more rapidly in the presence of oxidising agents (which absorb the hydrogen) like CrO3 and H2O2.
[10 bis] The addition of cupric sulphate, or, better still, a few drops of platinic chloride (the metals become reduced), to the sulphuric acid greatly accelerates the evolution of the hydrogen, because in this case, as with commercial zinc, galvanic couples are formed locally by the copper or platinum and the zinc, under the influence of which the zinc rapidly dissolves. The action of acids on metallic zinc of various degrees of purity has been the subject of many investigations, particularly important with reference to the application of zinc in galvanic batteries, whilst some investigations have direct significance for chemical mechanics, although from many points of view the matter is not clear. I consider it useful to mention certain of these investigations.
Calvert and Johnson made the following series of observations on the action of sulphuric acid of various degrees of concentration on 2 grams of pure zinc during two hours. In the cold the concentrated acid, H2SO4, does not act, H2SO4,2H2O dissolves about 0·002 gram, but principally forms hydrogen sulphide, which is obtained also when the dilution reaches H2SO4,7H2O, when 0·035 gram of zinc is dissolved. When largely diluted with water, pure hydrogen begins to be disengaged. H2SO4,2H2O at 130° gives a mixture of hydrogen sulphide and sulphurous anhydride dissolving 0·156 gram of zinc.
Bouchardat showed that if in a vessel made of glass or sulphur dilute sulphuric acid acting on a piece of zinc liberates one part of hydrogen, then the same acid with the same piece of zinc in the same time will liberate 4 parts of hydrogen if the vessel be made of tin—that is, zinc forms a galvanic couple with tin; in a leaden vessel 9 parts of hydrogen are set free, with a vessel of antimony or bismuth 13 parts, silver or platinum 38 parts, copper 50 parts, iron 43 parts. If a salt of platinum be added to the dilute sulphuric acid (1 part of acid and 12 parts of water), Millon determined that the rapidity of the action on the zinc is increased 149 times, and by the addition of copper sulphate is rendered 45 times greater than the action of pure sulphuric acid. The salts which are added are reduced to metals by the zinc, their contact serving to promote the reaction because they form local galvanic currents.
According to the observations of Cailletet, if, at the ordinary pressure, sulphuric acid with zinc liberates 100 parts of hydrogen, then with a pressure of 60 atmospheres 47 parts will be liberated and 1 part at a pressure of 120 atmospheres. With a reduced pressure under the receiver of an air-pump 168 parts are liberated. Helmholtz showed that a reduced pressure also exercises its influence on galvanic elements.
Debray, Löwel, and others showed that zinc liberates hydrogen and forms basic salts and zinc oxide with solutions of many salts—for instance, MCln, aluminium sulphate, and alum, Sodium and potassium carbonates scarcely act, because they form carbonates. The salts of ammonia act more strongly than the salts of potassium and sodium; the zinc remains bright. It is evident that this action is founded on the formation of double salts and basic salts.
The variation with concentration in the rate of the action of sulphuric acid on zinc (containing impurities) under otherwise uniform conditions is in evident connection with the electrical conductivity of the solution and its viscosity, although, when largely diluted, the action is almost proportional to the amount of acid in a known volume of the solution. Forging, casting the molten metal, and similar mechanical influences change the density and hardness of zinc, and also strongly influence its power of liberating hydrogen from acids. Kayander showed (1881) that when magnesium is submitted to the action of acids: (a) the action depends, not on the nature of the acid, but on its basicity; (b) the increase of the action is more rapid than the growth of the concentration; and (c) there is a decrease of action with the increase of the coefficient of internal friction and electrical conductivity.
Spring and Aubel (1887) measured the volume of hydrogen disengaged by an alloy of zinc and a small quantity of lead (0·6 p.c.), because the action of acids is then uniform. In order to deal with a known surface, spheres were taken (9·5 millimetres diameter) and cylinders (17 mm. dia.), the sides of which were covered with wax in order to limit the action to the end surfaces. During the commencement of the action of a definite quantity of acid the rapidity increases, attains a maximum, and then declines as the acid becomes exhausted. The results for 5, 10, and 15 per cent. of hydrochloric acid are given below. H denotes the number of cubic centimetres of hydrogen, D the time in seconds elapsing after the zinc spheres have been plunged into the acid. At 15° were obtained:
| H = | 50 | 100 | 200 | 400 | 600 | 800 | 1000 | |
| 5 p.c. | D = | 5714 | 1152 | 1755 | 2731 | 3908 | 6234 | 15462 |
| 10 p.c. | D = | 301 | 455 | 649 | 995 | 1573 | 2746 | 6748 |
| 15 p.c. | D = | 106 | 151 | 233 | 440 | 826 | 1604 | 4289 |
| At 35°: | ||||||||
| 5 p.c. | D = | 426 | 705 | 1058 | 1700 | 2525 | 4132 | 8499 |
| 10 p.c. | D = | 96 | 148 | 239 | 460 | 835 | 1594 | 3735 |
| 15 p.c. | D = | 44 | 64 | 112 | 255 | 505 | 1011 | 2457 |
| At 55°: | ||||||||
| 5 p.c. | D = | 178 | 276 | 408 | 699 | 1164 | 2105 | 5093 |
| 10 p.c. | D = | 34 | 60 | 113 | 258 | 491 | 970 | 2457 |
| 15 p.c. | D = | 24 | 35 | 58 | 136 | 239 | 610 | 1593 |