Put one part of small iron nails into a crucible, and set it amidst burning coals, in a melting furnace. When the iron is thoroughly red-hot, and begins to grow white, add thereto little by little, and at several times, two parts of crude Antimony in powder. The Antimony will immediately flow and unite with the Iron. When the Antimony is entirely melted, add thereto, at several times, the fourth of its weight of pulverized Nitre: a detonation will ensue, and the whole mixture will be in fusion.
After you have kept the matter in this condition for some minutes, pour it into an iron cone, first heated and tallowed. Strike the sides of the cone with a hammer, that the Regulus may fall to the bottom; and, when all is cold, separate it from the scoria by a blow with a hammer. Melt this first Regulus again in another crucible, adding a fourth part of its weight of crude Antimony. Keep the crucible close shut, and give no more heat than is necessary to melt the matter. When it is in perfect fusion, add to it at several times, as you did before, the sixth part of its weight of pulverized Nitre; and, in half a quarter of an hour after this, pour the whole into a cone as you did the first time.
Lastly, melt your Regulus over again a third, or even a fourth time, always adding a little Nitre, which will detonate as before. If after all these fusions you pour the Regulus into an iron cone, you will find it very beautiful, and the star well formed: it will be covered with a semi-transparent, lemon-coloured scoria. This scoria is extremely acrid and caustic.
OBSERVATIONS.
Though Regulus of Antimony unites very readily with Sulphur, and is always found combined therewith in the earth, we must not thence conclude that it hath a greater affinity than other substances with that mineral: on the contrary, all the metals, except Gold, have a greater affinity than this Semi-metal with Sulphur. Hence it follows that all the metals, except Gold, are capable of decomposing Antimony, and separating the sulphureous part from the metalline; so that, instead of employing Iron, as in our process, Copper, Lead, Tin, or Silver, may be used, and a Regulus obtained by means thereof.
But as Iron is, of all the metallic substances, that which hath the greatest affinity with Sulphur, it is on this occasion preferred to the rest. And from hence two advantages arise: the first is, that the operation is performed sooner and with greater ease: the second, that the Regulus is purer, and contains less of the precipitating metal. For it is a general rule, that, when one metallic substance is employed to precipitate another, the precipitated substance is always a little adulterated by the admixture of some particles of the precipitant. Now, the greater affinity the precipitant hath with the matter united to that which is to be precipitated, the less doth the precipitate retain of the precipitant.
In this process the Iron melts very easily by means of the union it contracts with the Sulphur; which, as we observed before, hath the property of rendering this metal very fusible, though of itself the most refractory of all.
The scoria found on the Regulus of the first fusion is a combination of Iron with the sulphureous part of the Antimony. This scoria is extremely hard, and not to be separated from the Regulus without some trouble. The Nitre added, being alkalizated and united therewith, renders it a little softer, and gives it the property of relenting in the air. Any Alkaline Salt may be substituted for the Nitre.
The Nitre that is alkalizated in the operation, or the Alkali that is added, procures moreover another advantage; namely, that, by uniting with part of the Sulphur of the Antimony, it produces a Liver of Sulphur, which dissolves the Iron, retains it, and hinders that which is not yet combined with pure Sulphur from uniting so readily with the Regulus as it otherwise would do.
Lastly, the addition of Nitre, or an Alkali, contributes greatly to promote the fusion, to render it more perfect, and to procure a more complete precipitation of the Regulus.