CRUCIBLES
It is often necessary in quantitative analysis to employ fluxes to bring into solution substances which are not dissolved by acids. The fluxes in most common use are sodium carbonate and sodium or potassium acid sulphate. In gravimetric analysis it is usually necessary to ignite the separated substance after filtration and washing, in order to remove moisture, or to convert it through physical or chemical changes into some definite and stable form for weighing. Crucibles to be used in fusion processes must be made of materials which will withstand the action of the fluxes employed, and crucibles to be used for ignitions must be made of material which will not undergo any permanent change during the ignition, since the initial weight of the crucible must be deducted from the final weight of the crucible and product to obtain the weight of the ignited substance. The three materials which satisfy these conditions, in general, are platinum, porcelain, and silica.
Platinum crucibles have the advantage that they can be employed at high temperatures, but, on the other hand, these crucibles can never be used when there is a possibility of the reduction to the metallic state of metals like lead, copper, silver, or gold, which would alloy with and ruin the crucible. When platinum crucibles are used with compounds of arsenic or phosphorus, special precautions are necessary to prevent damage. This statement applies to both fusions and ignitions.
Fusions with sodium carbonate can be made only in platinum, since porcelain or silica crucibles are attacked by this reagent. Acid sulphate fusions, which require comparatively low temperatures, can sometimes be made in platinum, although platinum is slightly attacked by the flux. Porcelain or silica crucibles may be used with acid fluxes.
Silica crucibles are less likely to crack on heating than porcelain crucibles on account of their smaller coefficient of expansion. Ignition of substances not requiring too high a temperature may be made in porcelain or silica crucibles.
Iron, nickel or silver crucibles are used in special cases.
In general, platinum crucibles should be used whenever such use is practicable, and this is the custom in private, research or commercial laboratories. Platinum has, however, become so valuable that it is liable to theft unless constantly under the protection of the user. As constant protection is often difficult in instructional laboratories, it is advisable, in order to avoid serious monetary losses, to use porcelain or silica crucibles whenever these will give satisfactory service. When platinum utensils are used the danger of theft should always be kept in mind.