Porcelain

by Edward Dillon

The English word ‘glaze’ is only another form of the word ‘glass,’ and we may say at once that, in composition at least, there is often little difference between the two substances. The French word for ‘glaze’ is couverte or vernis; the last term applies well to the thin skin of glaze found on Greek pottery. The Chinese have several expressions, but it is a curious fact that the characters with which most of these terms are written contain the radical for ‘oil,’ and indeed the word ‘oil’ itself is often used in the sense of ‘glaze.’

Mr. Rix puts it well when he says that the glaze is to the enameller of porcelain what his canvas is to the painter; while in the case of a decoration ‘sous couverte,’ the glaze corresponds to the varnish which, while protecting his work, gives brilliancy to the colouring (Journal of Society of Arts, vol. xli.). It is, moreover, the vehicle by which the design is harmonised and rendered mellow. The effect is produced at once and endures practically for all time.

The hardness and fusibility of glazes differ widely, and they are conditioned by the nature of the wares that they cover. It is evident that there must be a close relation between the fusing-points of paste and glaze, and that the latter should be the more fusible of the two. The difference of melting-point should, however, not be too great. The melted glaze should rather, by penetrating into the already softened paste or by a chemical action upon its surface, form a more or less uniform mass with it. In cooling, the contraction of the glaze should follow that of the subjacent paste. This is a most important point; any discordance may lead to splitting, cracking, and ‘crazing.’

The beauty of the surface of porcelain depends on the fact that the glaze has become intimately united with the paste during the long exposure of both to a high temperature. We should not be conscious, in regarding a fine specimen of porcelain, of a greater or less thickness of glass covering an opaque substance; we should rather see in it the polished surface of ivory or of some precious marble.

It would seem that it was the beauty of the glassy surface, enhancing the brilliancy of the colouring, rather than any practical advantage connected with its use, that first led to the application of glaze to pottery. The turquoise and green glazes of the Egyptians (the colour is derived from a silicate of copper along with soda and sometimes lime) were known to the men of the Early Empire. They were applied to a fritlike mass of sand held together by silicate of soda, to which the name of porcelain has sometimes been very wrongly given. Objects of steatite, of slate, and even of rock crystal were sometimes covered with a coloured glaze of this kind, but it was never applied to the clay vessels in daily use. These were made, then as now, from the unctuous clay of the Nile bank. For this restriction there was a very good reason, namely that a glaze of this nature, composed chiefly of alkaline silicates, will not adhere to a base of ordinary clay. It was not until Ptolemaic and Roman times that, by the discovery or adoption of a glaze containing lead, the ancients were enabled to glaze their pottery. So in Assyria, the employment of glazes was almost confined to the decoration of the surface of brickwork, the bricks being of a loose and somewhat sandy texture.[17]

In these glazes, and indeed in much earlier examples from Babylonia, both tin and lead have been found. The respective virtues of the silicates of these metals were doubtless appreciated, that of tin to form a white opaque enamel hiding the material below, and that of lead to enable the glaze into which it enters to adhere to a paste formed of a plastic clay.

With the Chinese the aim was rather æsthetic than practical. They sought by means of the marvellous glazes that cover their ancient porcelain to imitate the surface of natural stones; their early celadons were in a measure intended to take the place of the precious green jade, so highly esteemed by them.

At the time when the manufacture of porcelain was first introduced from China there were (apart from the salt-glazed stoneware, which lies quite outside our inquiry) three classes of glaze in general use either in Europe or in the nearer East:—

1. Glazes consisting essentially of alkaline silicates without either lead or tin. Such glazes could only be applied to a fritty silicious base, and in India and Persia their employment seems to have been a survival from Egyptian and Assyrian times.[18]

2. Opaque enamel glazes, the opacity being due to the presence of tin; a considerable amount of lead also is generally found in these glazes. We are not concerned here with the obscure origin of this group, but in the sixteenth century this enamelled fayence was in general use for the better class of table-ware. It includes the Italian majolica, the French fayence of Nevers and Rouen, and above all the earthenware of Delft.