To bring out the full qualities of nickel it must be heat-treated, otherwise there is no object in using nickel as an alloy with carbon steel as the additional cost is not justified by increased strength.
Nickel has a peculiar effect upon the critical ranges of steel, the critical range being lowered by the percentage of nickel; in this respect it is similar to manganese.
Nickel can be alloyed with steel in various percentages, each percentage having a very definite effect on the microstructure. For instance, a steel with 0.2 per cent carbon and 2 per cent nickel has a pearlitic structure but the grain is much finer than if the straight carbon were used. With the same carbon content and say 5 per cent nickel, the structure would still be pearlitic, but much finer and denser, therefore capable of withstanding shock, and having greater dynamic strength. With about 0.2 per cent carbon and 8 per cent nickel, the steel is nearing the stage between pearlite and martensite, and the structure is extremely fine, the ferrite and pearlite having a very pronounced tendency to mimic a purely martensite structure. Steel with 0.2 per cent carbon and 15 per cent nickel is entirely martensite. Higher percentages of nickel change the martensitic structure to austenite, the steel then being non-magnetic. The higher percentages, that is 30 to 35 per cent nickel, are used for valve seats, valve heads, and valve stems, as the alloy is a poor conductor of heat and is particularly free from any tendency towards corrosion or pitting from the action of waste gases of the internal-combustion engine.
Nickel steels having 3½ per cent nickel and 0.15 to 0.20 per cent carbon are excellent for case-hardening purposes, giving hard surfaces and tough interiors.
To obtain the full effect of nickel as an alloy, it is essential that the correct percentage of carbon be used. High nickel and low carbon will not be more efficient than lower nickel and higher carbon, but the cost will be much greater. Generally speaking, heat-treated nickel alloy steels are about two to three times stronger than the same steel annealed. This point is very important as many instances have been found where nickel steel is incorrectly used, being employed when in the annealed or normal state.
CHROMIUM
Chromium when alloyed with steel, has the characteristic function of opposing the disintegration and reconstruction of cementite. This is demonstrated by the changes in the critical ranges of this alloy steel taking place slowly; in other words, it has a tendency to raise the Ac range (decalescent points) and lower the Ar range (recalescent points). Chromium steels are therefore capable of great hardness, due to the rapid cooling being able to retard the decomposition of the austenite.
The great hardness of chromium steels is also due to the formation of double carbides of chromium and iron. This condition is not removed when the steel is slightly tempered or drawn. This additional hardness is also obtained without causing undue brittleness such as would be obtained by any increase of carbon. The degree of hardness of the lower-chrome steels is dependent upon the carbon content, as chromium alone will not harden iron.
The toughness so noticeable in this steel is the result of the fineness of structure; in this instance, the action is similar to that of nickel, and the tensile strength and elastic limit is therefore increased without any loss of ductility. We then have the desirable condition of tough hardness, making chrome steels extremely valuable for all purposes requiring great resistance to wear, and in higher-chrome contents resistance to corrosion. All chromium-alloy steels offer great resistance to corrosion and erosion. In view of this, it is surprising that chromium steels are not more largely used for structural steel work and for all purposes where the steel has to withstand the corroding action of air and liquids. Bridges, ships, steel building, etc., would offer greater resistance to deterioration through rust if the chromium-alloy steels were employed.
Prolonged heating and high temperatures have a very bad effect upon chromium steels. In this respect they differ from nickel steels, which are not so affected by prolonged heating, but chromium steels will stand higher temperatures than nickel steels when the period is short.