Another advantage obtained from rapid cooling from the carbonizing heat is the retaining of the majority of the excess cementite in solution which produces a less brittle case and by so doing reduces the liability of grinding checks and chipping of the case in actual service.
In the case of the camshaft, it is not possible to quench directly from the carbonizing heat because of distortion and therefore excessive breakage during straightening operations. All Liberty camshafts were cooled slowly from carbonizing heat and hardened by a single reheating to a temperature of from 1,380 to 1,430°F. and quenching in water.
Considerable trouble has always been experienced in obtaining uniform hardness on finished camshafts. This is caused by insufficient water circulation in the quenching tank, which allows the formation of steam pockets to take place, or by decarbonization of the case during heating by the use of an overoxidizing flame. Another cause, which is very often overlooked, is due to the case being ground off one side of cam more than the other and is caused by the roughing master cam being slightly different from the finishing master cam. Great care should be taken to see that this condition does not occur, especially when the depth of case is between 1/32 and 3/64 in.
CARBON-STEEL FORGINGS
Low-stressed, carbon-steel forgings include such parts as carbureter control levers, etc. The important criterion for parts of this type is ease of fabrication and freedom from over-heated and burned forgings. The material used for such parts was S. A. E. No. 1,030 steel, which is of the following chemical composition: Carbon, 0.250 to 0.350 per cent; manganese, 0.500 to 0.800 per cent; phosphorus, 0.045 maximum per cent; sulphur, 0.050 maximum per cent.
To obtain good machineability, all forgings produced from this steel were heated to a temperature of from 1,575 to 1,625°F. to refine the grain of the steel thoroughly and quenched in water and then tempered to obtain proper machineability by heating to a temperature of from 1,000 to 1,100°F. and cooled slowly or quenched.
Forgings subjected to this heat treatment are free from hard spots and will show a Brinell hardness of 177 to 217, which is proper for all ordinary machining operations. Great care should be taken not to use steel for parts of this type containing less than 0.25 per cent carbon, because the lower the carbon the greater the liability of hard spots, and the more difficult it becomes to eliminate them. The only satisfactory method so far in commercial use for the elimination of hard spots is to give forgings a very severe quench from a high temperature followed by a proper tempering heat to secure good machine ability as outlined above.
The important carbon-steel forgings consisted of the cylinders, the propeller-hubs, the propeller-hub flange, etc. The material used for parts of this type was S. A. E. No. 1,045 steel, which is of the following chemical composition: Carbon, 0.400 to 0.500 per cent; manganese, 0.500 to 0.800 per cent; phosphorus, 0.045 maximum per cent; sulphur, 0.050 maximum per cent.
All forgings made from this material must show, after heat treatment, the following minimum physical properties: Elastic limit, 70,000; lb. per square inch, elongation in 2 in., 18 per cent, reduction of area, 45; per cent, Brinell hardness, 217 to 255.
To obtain these physical properties, the forgings were quenched in water from a temperature of 1,500 to 1,550°F., followed by tempering to meet proper Brinell requirements by heating to a temperature of 1,150 to 1,200°F. and cooled slowly or quenched. No trouble of any kind was ever experienced with parts of this type.