There is no question but that a gear made from material of such an analysis will give excellent service. However, it is possible to obtain the same quality of service and at the same time appreciably reduce the cost of the finished part. The gear steel specified is of the air-hardening type. It is extremely sensitive to secondary pipe, as well as seams, and is extremely difficult to forge and very easy to overheat. The heat-treatment range is very wide, but the danger from quenching cracks is very great. In regard to the machineability, this material is the hardest to machine of any alloy steel known.
COMPOSITION OF TRANSMISSION-GEAR STEEL
If the nickel content of this steel is eliminated, and the percentage of chromium raised slightly, an ideal transmission-gear material is obtained. This would, therefore, be of the following composition: Carbon, 0.470 to 0.520 per cent; manganese, 0.500 to 0.800 per cent; phosphorus, 0.040 maximum per cent; sulphur, 0.045 maximum per cent; chromium, 0.800 to 1.100 per cent.
The important criterion in connection with the use of this material is that the steel be properly deoxidized, either through the use of ferrovanadium or its equivalent. Approximately 2,500 sets of transmission gears are being made daily from material of this analysis and are giving entirely satisfactory results in service. The heat treatment of the above material for transmission gears is as follows: "Normalize forgings at a temperature of from 1,5.50 to 1,600°F. Cool from this temperature to a temperature of 1,100°F. at the rate of 50° per hour. Cool from 1,100°F., either in air or quench in water."
Forgings so treated will show a Brinell hardness of from 177 to 217, which is the proper range for the best machineability. The heat treatment of the finished gears consists of quenching in oil from a temperature of 1,500 to 1,540°F., followed by tempering in oil at a temperature of from 375 to 425°F. Gears so treated will show a Brinell hardness of from 512 to 560, or a scleroscope hardness of from 72 to 80. One tractor builder has placed in service 20,000 sets of gears of this type of material and has never had to replace a gear. Taking into consideration the fact that a tractor transmission is subjected to the worst possible service conditions, and that it is under high stress 90 per cent of the time, it seems inconceivable that any appreciable transmission trouble would be experienced when material of this type is used on an automobile, where the full load is applied not over 1 per cent of the time, or on trucks where the full load is applied not over 50 per cent of the time.
The gear hardness specified is necessary to reduce to a minimum the pitting or surface fatigue of the teeth. If gears having a Brinell hardness of over 560 are used, danger is encountered, due to low shock-resisting properties. If the Brinell hardness is under 512, trouble is experienced due to wear and surface fatigue of the teeth.
For ring gears and pinions material of the following chemical composition is recommended: Carbon, 0.100 to 0.200 per cent; manganese, 0.350 to 0.650 per cent; phosphorus, 0.040 maximum per cent; sulphur, 0.045 maximum per cent; chromium, 0.550 to 0.750 per cent; nickel, 0.400 to 0.600 per cent.
Care should be taken to see that this material is properly deoxidized either by the use of ferrovanadium or its equivalent. The advantage of using a material of the above type lies in the fact that it will produce a satisfactory finished part with a very simple treatment. The heat treatment of ring gears and pinions is as follows: "Carburize at a temperature of from 1,650 to 1,700°F. for a sufficient length of time to secure a depth of case of from 1/32 to 3/64 in., and quench directly from carburizing heat in oil. Reheat to a temperature of from 1,430 to 1,460°F. and quench in oil. Temper in oil at a temperature of from 375 to 425°F. The final quenching operation on a ring gear should be made on a fixture similar to the Gleason press to reduce distortion to a minimum."
One of the largest producers of ring gears and pinions in the automotive industry has been using this material and treatment for the last 2 years, and is of the opinion that he is now producing the highest quality product ever turned out by that plant.
On some designs of automobiles a large amount of trouble is experienced with the driving pinion. If the material and heat treatment specified will not give satisfaction, rather than to change the design it is possible to use the following analysis material, which will raise the cost of the finished part but will give excellent service: Carbon, 0.100 to 0.200 per cent; manganese, 0.350 to 0.650 per cent; phosphorus, 0.040 maximum per cent; sulphur, 0.045 maximum per cent; nickel, 4.750 to 5.250 per cent.