In order to use the chart it is necessary to harden the sample we desire to test as we would harden a piece of tool steel, and then test by scleroscope. By locating on the chart the point on the horizontal axis which represents the hardness of the sample the curve enables one to determine the approximate amount of carbon present in the case.
Should the hardness lack uniformity the soft places can be identified by etching. To accomplish this the sample should be polished after quenching and then washed with a weak solution of nitric acid in alcohol, whereupon the harder points will show up darker than the softer areas.
The selection of suitable boxes for carburizing is worthy of a little consideration, and there can be no doubt that in certain cases results are spoiled and considerable expense caused by using unsuitable containers.
As far as initial expense goes cast-iron boxes are probably the most expedient, but although they will withstand the necessary temperatures they are liable to split and crack, and when they get out of shape there is much difficulty in straightening them.
The most suitable material in most cases is steel boiler plate 3/8 or 1/2 in. thick, which can be made with welded joints and will last well.
The sizes of the boxes employed depend to a great extent on the nature of the work being done, but care should be exercised to avoid putting too much in one box, as smaller ones permit the heat to penetrate more quickly, and one test piece is sufficient to give a good indication of what has taken place. If it should be necessary to use larger boxes it is advisable to put in three or four test pieces in different positions to ascertain if the penetration of carbon has been satisfactory in all parts of the box, as it is quite possible that the temperature of the muffle is not the same at all points, and a record shown by one test piece would not then be applicable to all the parts contained in the box. It has been found that the rate of carbon penetration increases with the gas pressure around the articles being carburized, and it is therefore necessary to be careful in sealing up the boxes after packing. When the articles are placed within and each entirely surrounded by compound so that the compound reaches to within 1 in. of the top of the box a layer of clay should be run around the inside of the box on top of the compound. The lid, which should be a good fit in the box, is then to be pressed on top of this, and another layer of clay run just below the rim of the box on top of the cover.
A SATISFACTORY LUTING MIXTURE
A mixture of fireclay and sand will be found very satisfactory for closing up the boxes, and by observing the appearance of the work when taken out we can gage the suitability of the methods employed, for unless the boxes are carefully sealed the work is generally covered with dark scales, while if properly done the articles will be of a light gray.
By observing the above recommendations reliable results can be obtained, and we can expect uniform results after quenching.