DETERMINATION OF PHOSPHORIC ANHYDRIDE IN APATITE
The mineral apatite is composed of calcium phosphate, associated with calcium chloride, or fluoride. Specimens are easily obtainable which are nearly pure and leave on treatment with acid only a slight siliceous residue.
For the purpose of gravimetric determination, phosphoric acid is usually precipitated from ammoniacal solutions in the form of magnesium ammonium phosphate which, on ignition, is converted into magnesium pyrophosphate. Since the calcium phosphate of the apatite is also insoluble in ammoniacal solutions, this procedure cannot be applied directly. The separation of the phosphoric acid from the calcium must first be accomplished by precipitation in the form of ammonium phosphomolybdate in nitric acid solution, using ammonium molybdate as the precipitant. The "yellow precipitate," as it is often called, is not always of a definite composition, and therefore not suitable for direct weighing, but may be dissolved in ammonia, and the phosphoric acid thrown out as magnesium ammonium phosphate from the solution.
Of the substances likely to occur in apatite, silicic acid alone interferes with the precipitation of the phosphoric acid in nitric acid solution.
PRECIPITATION OF AMMONIUM PHOSPHOMOLYBDATE
PROCEDURE.—Grind the mineral in an agate mortar until no grit is perceptible. Transfer the substance to a weighing-tube, and weigh out two portions, not exceeding 0.20 gram each (Note 1) into two beakers of about 200 cc. capacity. Pour over them 20 cc. of dilute nitric acid (sp. gr. 1.2) and warm gently until solvent action has apparently ceased. Evaporate the solution cautiously to dryness, heat the residue for about an hour at 100-110°C., and treat it again with nitric acid as described above; separate the residue of silica by filtration on a small filter (7 cm.) and wash with warm water, using as little as possible (Note 2). Receive the filtrate in a beaker (200-500 cc.). Test the washings with ammonia for calcium phosphate, but add all such tests in which a precipitate appears to the original nitrate (Note 3). The filtrate and washings must be kept as small as possible and should not exceed 100 cc. in volume. Add aqueous ammonia (sp. gr. 0.96) until the precipitate of calcium phosphate first produced just fails to redissolve, and then add a few drops of nitric acid until this is again brought into solution (Note 4). Warm the solution until it cannot be comfortably held in the hand (about 60°C.) and, after removal of the burner, add 75 cc. of ammonium molybdate solution which has been !gently! warmed, but which must be perfectly clear. Allow the mixture to stand at a temperature of about 50 or 60°C. for twelve hours (Notes 5 and 6). Filter off the yellow precipitate on a 9 cm. filter, and wash by decantation with a solution of ammonium nitrate made acid with nitric acid.[1] Allow the precipitate to remain in the beaker as far as possible. Test the washings for calcium with ammonia and ammonium oxalate (Note 3).
[Footnote 1: This solution is prepared as follows: Mix 100 cc. of ammonia solution (sp. gr. 0.96) with 325 cc. of nitric acid (sp. gr. 1.2) and dilute with 100 cc. of water.]
Add 10 cc. of molybdate solution to the nitrate, and leave it for a few hours. It should then be carefully examined for a !yellow! precipitate; a white precipitate may be neglected.
[Note 1: Magnesium ammonium phosphate, as noted below, is slightly soluble under the conditions of operation. Consequently the unavoidable errors of analysis are greater in this determination than in those which have preceded it, and some divergence may be expected in duplicate analyses. It is obvious that the larger the amount of substance taken for analysis the less will be the relative loss or gain due to unavoidable experimental errors; but, in this instance, a check is placed upon the amount of material which may be taken both by the bulk of the resulting precipitate of ammonium phosphomolybdate and by the excessive amount of ammonium molybdate required to effect complete separation of the phosphoric acid, since a liberal excess above the theoretical quantity is demanded. Molybdic acid is one of the more expensive reagents.]
[Note 2: Soluble silicic acid would, if present, partially separate with the phosphomolybdate, although not in combination with molybdenum. Its previous removal by dehydration is therefore necessary.]