Elements of the Theory and Practice of Chymistry, 5th ed.

by Pierre Joseph Macquer

The refining of Silver by the Cupel.

Take a cupel capable of containing one third more matter than you have to put into it: set it under the muffle of a furnace, like that described in our Theoretical Elements, as peculiarly appropriated to this sort of operation. Fill the furnace with charcoal; light it; make the cupel red-hot, and keep it so till all its moisture be evaporated; that is, for about a good quarter of an hour, if the cupel be made wholly of the ashes of burnt bones; and for a whole hour, if there be any washed wood-ash in its composition.

Reduce the Regulus which remained after the preceding operation to little thin plates, flatting them with a small hammer, and separating them carefully from all the adherent scoria. Wrap these in a bit of paper, and with a small pair of tongs put them gently into the cupel. When the paper is consumed the Regulus will soon melt, and the scoria, which will be gradually produced by the Lead as it turns to litharge, will be driven to the sides of the cupel, and immediately absorbed thereby. At the same time the cupel will assume a yellow, brown, or blackish colour, according to the quantity and nature of the scoria imbibed by it.

When you see the matter in the cupel in a violent ebullition, and emitting much smoke, lower the fire by the methods formerly prescribed. Keep up such a degree of heat only that the smoke which ascends from the matter may not rise very high, and that you may be able to distinguish the colour which the cupel acquires from the scoria.

Increase the fire by degrees, as more and more litharge is formed and absorbed. If the Regulus examined by this assay contain no Silver, you will see it turn wholly into scoria, and at last disappear. When it contains Silver, and the quantity of Lead is much diminished, you will perceive little vivid irises, or beautiful rain-bow colours, shooting swiftly along its surface, and crossing each other in many different directions. At last, when all the Lead is destroyed, the thin dark skin, that is continually protruded by the Lead while it is turning into litharge, and which hitherto covered the Silver, suddenly disappears; and, if at this moment the fire happen not to be strong enough to keep the Silver in fusion, the surface of that metal will at once dart out a dazzling splendour: but, if the fire be strong enough to keep the Silver in fusion, though freed from all mixture of Lead, this change of colour, which is called its fulguration, will not be so perceptible, and the Silver will appear like a bead of fire.

These phenomena shew that the operation is finished. But the cupel must still be left a minute or two under the muffle, and then drawn slowly out with the iron hook towards the door of the furnace. When the Silver is so cooled as to be but moderately red, you may take the cupel from under the muffle with your little tongs, and in the middle of its cavity you will find an exceeding white bead of Silver, the lower part whereof will be unequal, and full of little pits.

OBSERVATIONS.

The Regulus obtained by the former process consists altogether of the Silver contained in the ore, alloyed with the other metals that happened to be mixed therewith in its mineral state, and a good deal of the Lead that was added to precipitate the Silver. The operation of the cupel may be considered as the sequel of that process, being intended only to reduce into a scoria whatever is not Gold or Silver. Lead being of all metals that which vitrifies the most easily, which most promotes the vitrification of the rest, and the only one which, when vitrified, penetrates the cupel, and carries along with it the other metals which it hath vitrified, is consequently the fittest for that purpose. We shall see in its place, that Bismuth hath the same properties with Lead, and may be substituted for it in this operation.

Care must be taken to chuse a cupel of a proper capacity. Indeed it should rather be too big than too little: because the operation is no way prejudiced by an excess in its size; whereas, if it be too small, it will be over-dosed with Lead, and at last the litharge, which destroys every thing, will corrode its cavity, and eat holes through the very body of the vessel. Add, that the ashes, of which the cupel is made, being once glutted with litharge, absorb it afterwards but slowly, and that the quantity of this vitrified litharge, becoming too great to be contained in the substance of the vessel, exsudes through it, and drops on the floor of the muffle, which it corrodes and renders unequal; and moreover solders to it the vessels set thereon. It may be laid down as a general rule for determining the size of a cupel, that it weigh, at least, half as much as the metallic mass to be refined in it.