It is also of the utmost consequence that the cupel be well dried before the metal be put into it. In order to make sure of this point, it must be kept red-hot for a certain time, as is above directed: for though to the sight and to the touch it may appear very dry, it nevertheless obstinately retains a small matter of moisture, sufficient to occasion the loss of some of the metal; which, when it comes to melt, will be thereby spirited up, in the form of little globules, to the very roof of the muffle. The cupels that stand most in need of an intense heat to dry them, are those chiefly in whose composition wood-ashes are employed: for whatever care be taken to lixiviate those ashes before they are used, they will still retain a little alkaline salt; and that, we know, is very greedy of moisture, will not part entirely with it, but by the means of a violent calcination, and presently re-imbibes it when exposed to the air.

A little Phlogiston also may still be left in the ashes of which the cupels are made; and that is another reason for calcining them before they are used. By this means the remaining Phlogiston is dissipated, which might otherwise combine with the litharge during the operation, reduce it, and occasion such a ferment in the matter as to make some of it run over; to these inconveniencies, which any remainder of moisture or Phlogiston may produce, we must add the cracks and flaws, which are very incident to cupels not perfectly freed from both those matters.

It is of no less importance to the success of this operation, that a due degree of heat be kept up. In the process we have described the marks which shew the heat to be neither too strong nor too weak; when it exceeds in either of these respects it may be known by the following signs.

If the fume emitted by the Lead rise like a spout to the roof of the muffle; if the surface of the melted metal be extremely convex, considering the quantity of the mass: if the cupel appear of such a white heat, that the colour communicated thereto by the imbibed scoria cannot be distinguished: all these shew that the heat is too great, and that it ought to be diminished. If, on the contrary, the vapours only hover, as it were, over the surface of the metal; if the melted mass be very flat, considering its quantity; if its ebullition appear but faint; if the scoriæ, that appear like little fiery drops of rain, have but a languid motion; if the scoria gather in heaps, and do not penetrate the cupel; if the metal be covered with it as with a glassy coat; and, lastly, if the cupel look dull; these are proofs that the heat is too weak, and ought to be increased.

The design of this operation being to convert the Lead into litharge, and to give it sufficient time and opportunity to scorify and carry off with it whatever is not Gold or Silver; the fire must be kept up to such a degree that the Lead may easily be turned into litharge, and yet that litharge not be absorbed too hastily by the cupel, but that a small quantity thereof may all along remain, like a ring, round the melted metal.

The fire is to be gradually increased as the operation draws nearer to its end: for, as the proportion of the Lead to the Silver is continually lessening, the metallic mass gradually becomes less fusible; while the Silver defends the Lead mixed with it from the action of the fire, and prevents its being easily converted into litharge.

When the operation is finished, the cupel must still be left under the muffle, till it has imbibed all the litharge, to the end that the bead of Silver may be easily taken out: for, without this precaution, it would stick so fast as not to be removed, but by breaking off part of the cupel along with it. Care must also be taken to let this bead of Silver cool gradually, and be perfectly fixed, before you draw it from under the muffle; for if you expose it at once to the cold air, before it be fixed, it will swell, shoot into sprigs, and even dart out several little grains to a considerable distance, which will be lost.

If the bead appear to have a yellowish tinge, it is a sign that it contains a great deal of Gold, which must be separated from it by the methods to be hereafter shewn.

It is proper to observe, that there is scarce any Lead that does not contain some Silver; too little perhaps to defray the charges necessary to separate it, yet considerable enough to lead us into an error, by mixing with the Silver obtained from an ore, and increasing its weight. And therefore, when the operations above described are applied to the assaying of an ore, in order to know how much Silver it yields, it is previously necessary to examine the Lead to be used, and to ascertain the quantity of Silver it contains, which must be deducted from the total weight of the bead of Silver obtained by purifying it in this manner.

Silver may be separated from its ore, and at the same time refined, by the single operation of the cupel, without any previous scorification with Lead. In order to do this, you must pound the ore; roast it, to dissipate all its volatile parts; mix it with an equal quantity of litharge, if it be refractory; divide it into five or six parcels, wrapping each in a bit of paper; weigh out eight parts of granulated Lead for one of ore, if it be fusible, and from twelve to sixteen, if it be refractory; put one half of the Lead into a very large cupel under the muffle; add thereto one of the little parcels of ore, when the Lead begins to smoke and boil; immediately slacken the fire a little; continue the same degree of heat till you perceive that the litharge formed round the metal, and on its surface, begins to look bright; then raise the fire; add a fresh parcel of ore; continue proceeding in the same manner till you have put in all the ore; then add the remaining half of the granulated Lead, and conduct the succeeding part of the operation in the same manner as that of cupelling.